點擊圖片查看大圖| NYLON 6 復合材料特性及應用 | ||||||||||
| 經(jīng)濟型NYLON6復合材料 Economical Nylon 6 Composite | NYLON6加纖型(BR) Glass Fiber& Reinforced | |||||||||
| 物性Properties | 單位Unit | 品名Grade規(guī)范ASTM | N11G 154N-D | N11G 204N-D | N11G 254N-D | N11G 334N-D | N11G 404N-D | N11G 454N-D | N11G 504N-D | |
| 抗張強度Tensile Strength | Kg/cm2 | D-635 | 1000 | 1200 | 1300 | 1500 | 1700 | 1650 | 1800 | |
| 伸長率Elongation | % | D-635 | 3.5 | 3 | 3 | 2.7 | 2.5 | 2.5 | 2.5 | |
| 抗折強度Flexural Strength | Kg/cm2 | D-790 | 1700 | 1800 | 2000 | 2200 | 2600 | 2600 | 2800 | |
| 抗折模數(shù)Flexural Modulus | Kg/cm2 | D-790 | 51000 | 61000 | 71000 | 82000 | 100000 | 110000 | 120000 | |
| 動擊強度Izod | kg-cm/cm | RT | D-256 | 6 | 7 | 10 | 14 | 16 | 15 | 19 |
| 硬度Hardness | Rockwell R | D-785 | 116 | 117 | 118 | 118 | 119 | 119 | 120 | |
| 熱變形溫度H D T | ℃ | 1.82Mpa | D-648 | 195 | 200 | 205 | 208 | 210 | 210 | 213 |
| 灰份Filler Content | % | D-2584 | 15 | 20 | 25 | 33 | 40 | 45 | 50 | |
| 比重Specific Gravity | D-792 | 1.23 | 1.26 | 1.31 | 1.38 | 1.45 | 1.49 | 1.54 | ||
| 模收縮率Mold Shrinkage | cm/cm | D-955 | 0.3-0.5 | 0.2-0.4 | 0.1-0.3 | 0.15-0.35 | 0.1-0.3 | 0.1-0.3 | 0.1-0.3 | |
| 特性:1.具高機械強度 | 成型條件: | |||||||||
| 2.耐韌及耐動擊性特優(yōu) | 1.干燥溫度時間100℃/3HRS | |||||||||
| 3.電氣特性佳 | 2.成型溫度:230-260℃ | |||||||||
| 4.耐化學藥品性佳 | 3.模具溫度:50-70℃ | |||||||||
| 5.耐磨擦性佳 | ||||||||||
| 備注:以上數(shù)值系參考ASTM試驗方法所測得,僅供選擇用途品級之參考. | ||||||||||
供應加纖型PA6塑膠原料