耐老化MS日本新日鐵住金MS-600
| 性能項目 | 測試條件 | 測試方法 | 數(shù)值/描述 | 單位 | |
| 機械性能 | 拉伸強度(引張強度) | ASTM D638/ISO 527 | 70 | kg/cm2(MPa)[Lb/in2] | |
| 斷裂伸長率 | ASTM D638/ISO 527 | % | |||
| 拉伸模量 | ASTM D638/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
| 拉伸屈服伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
| 拉伸斷裂伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
| 彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 3330 | kg/cm2(MPa)[Lb/in2] | ||
| 彎曲強度 | ASTM D790/ISO 178 | 116 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | 85 | |||
| IZOD 缺口沖擊強度 | 1/4" 23℃ | ASTM D256/ISO 179 | 2.5 | kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| Charpy沖擊強度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 23℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重（密度） | 1.13 | |||
| 熔融指數(shù)（流動系數(shù)） | 200℃/5kg | ASTM D1238/ISO 1133 | 1.0 | g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 成型收縮率 | ASTM D955 | 0.2-0.6 | % | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | % | |||
| 熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | ℃（℉） | |
| 未退火 | ASTM D648/ISO 75 | ℃（℉） | |||
| 維卡軟化點 | ASTM D1525/ISO R306 | 103 | ℃（℉） | ||
| 熔點 | - | ℃（℉） | |||
| 燃燒性（率） | UL94 | ||||
| 線性膨脹系數(shù) | ASTM D696/ISO 11359 | mm/mm.℃ | |||
| 加工條件 | 干燥條件 | ||||
| 加工溫度 | 射嘴 | ℃ | |||
| 料筒前段 | ℃ | ||||
| 料筒中段 | ℃ | ||||
| 料筒后段 | ℃ | ||||
| 熔體溫度 | ℃ | ||||
| 模具溫度 | ℃ | ||||
| 壓力 | 注塑壓力 | Mpa | |||
| 保壓壓力 | Mpa | ||||
| 背壓 | Mpa | ||||
| 螺桿轉速 | rpm | ||||
| 其他 | 備注 | ||||
| 顏色 | |||||
| 特性 | |||||
|
用途 |
|||||