①原料描述部分
| 其它 薄膜 擠出 | ||
| 薄膜，吹塑成型應(yīng)用，鑄造薄膜 | ||
| 芳香,高彈性 | ||
③原料技術(shù)數(shù)據(jù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
|
?
物理性能
|
比重 | ? | ASTM D-792 | 1.22 | g/cm3 |
| 熔流率 | 190°C/8.7 kg | ASTM D-1238 | 14 | g/10 min | |
| 硬度計(jì)硬度 | 支撐 A, 5 秒 | ASTM D-2240 | 85 | ? | |
|
? ? ??
機(jī)械性能
|
抗泰伯磨耗 | 1000 Cycles, 1000 g, H-18 轉(zhuǎn)輪 | ASTM D-3389 | 40.0 | mg |
| 拉伸變形 | 200% 應(yīng)變 | ASTM D-412 | 18 | % | |
| 水氣透過(guò)率? | 3°C, 90% RH 1 | ASTM D-6701 | 3000 | g/m2/24 hr | |
| ? | 23°C, 50% RH 2 | ASTM E96 | 500 | g/m2/24 hr | |
| 拉伸應(yīng)力 | 應(yīng)變 | ASTM D-412 | 6.21 | MPa | |
| ? | 300%應(yīng)變 | ASTM D-412 | 13.8 | MPa?? | |
| 抗張強(qiáng)度 | 斷裂 | ASTM D-412 | 34.5 | MPa | |
| 伸長(zhǎng)率 | 斷裂 | ASTM D-412 | 550 | % | |
| 撕裂強(qiáng)度 | -- 3 | ASTM D-624 | 78.8 | kN/m | |
| ? | 開(kāi)裂 | ASTM D-470 | 20 | kN/m | |
| 壓縮變形 | 23°C, 22.0 hr | ASTM D-395 | 17 | % | |
| ? | 70°C, 22.0 hr | ASTM D-395 | 79 | % | |
| 老化 | 體積變化 | 23°C, 24 hr | ASTM D-471 | 40 | % |
| ?熱性能 | 玻璃轉(zhuǎn)化溫度 | DSC | Internal Method | -23.9 | ℃ |
| 熔融溫度 | ? | Internal Method | 144 | ℃ | |
| ? | ? | Internal Method | 155 | ℃ | |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。