| LCP 350G6 | |||||
| 性能 | Properties |
測試標準 Standard |
測試條件 Condition | 單位 Unit | 數(shù)值 Value |
| 物理性能 | Physical Properties | ||||
| 密度 | Specific Gravity | ASTM D792 | 23℃ | g/cm3 | 1.61 |
| 成型收縮 | Mold Shrinkage | ASTM D955 | Cold mold, 48 hrs | % | 0.2-0.3 |
| 吸水率 | Moisture Absorption | ASTM D570 | 23 °C; 50 % RH | % | 0.2 |
| 填充量 | Filler Content, Glass Fiber | 800°C/2h | % | 30 | |
| 機械性能 | Mechanical Properties | ||||
| 拉伸強度 | Tensile Strength | ASTM D638 | 50mm/min | Mpa | 145 |
| 斷裂伸長率 | Elongation at Break | ASTM D638 | 50mm/min | % | 1.5 |
| 彎曲強度 | Flexural Strength | ASTM D790 | 20mm/min | Mpa | 190 |
| 彎曲模量 | Flexural Modulus | ASTM D790 | 20mm/min | Mpa | 13500 |
| 懸臂梁沖擊強度 | Izod Impact, Notched | ASTM D256 | J/m | 70 | |
| 熱性能 | Thermal Properties | ||||
| 熔點 | Melting Point | DSC | 23℃ | ℃ | 330 |
| 熱傳導率 | Thermal Conductivity | ASTM C177 | W/mK | 0.25 | |
| 熱膨脹系數(shù) | CTE | ASTM D696 | -20~150°C | μm/m℃ | / |
| 熱變形溫度 | HDT | ASTM D648 | 1.8 Mpa | ℃ | 280 |
| 阻燃性能 | Flammability | UL94 | 1.6 mm | V0 | |
| 電性能 | Electrical Properties | ||||
| 介電常數(shù) | PictPictDielectric Constant | IEC 60250 | 1 MHz | 3.9 | |
| 介電強度 | Dielectric Strength | IEC 60243 | S/T, in oil | kV/mm | 37 |
| 功耗因數(shù) | Dissipation Factor | IEC 60250 | 1 MHz | 0.003 | |
| 體積電阻率 | Volume Resistivity | IEC 60093 | 23℃ | ohm·cm | >1015 |
| *產(chǎn)品350G6由LCP+30% Glass Fiber組成的高強度LCP復合材料，適合注塑或者擠出等工藝。 | |||||